Abstract :

: This research highlights the contribution to the study of the microstructural quality of reinforcing bars on the Lubumbashi market including bars imported from South Africa (FA), Zambia (FZ) and those produced locally ( FC) by the only steel industry, in the former province of Katanga, the iron processing company SOTRAFER, in acronym.

The samples of the locally produced reinforcement bars (FC) were collected at SOTRAFER at the end of production, while the samples of the FA and FZ reinforcement bars were taken randomly on the Lushois market in a hardware store specializing in sales to avoid errors.Microstructural analysis of all bars revealed a similar microstructure consisting of a ferrite (light areas) and pearlite (dark areas) matrix and a ferrito-pearlitic structure. This microstructure, as predicted by the Fe-C equilibrium diagram, could be justified by the carbon content (lower than the eutectoid point content); the results prove that all bars are hypoeutectoid steels (%C ≤ 0.77). They can also be assimilated to the category of mild steels (0.1 ≤ %C ≤ 0.25). This also shows that all the bars have not undergone a particular heat treatment and have been cooled very slowly in order to allow the diffusion of atoms and reach equilibrium conditions. The results obtained from the variance analyses of different materials of dimensions of 10, 12 and 16 mm revealed that at the level of chemical and mechanical analyses, there was no significant difference on all the parameters studied and that all the reinforcement bars could perfectly be used in construction. Finally, the survey reveals that FA is reputed to be of better quality among consumers, for several reasons including the psychological one although its price is lower than that produced locally.

---

Keywords :

Equivalent carbon, Hypoeutectoids, microstructure, Reinforcement bars.

---

References :

1. Jean Pierre B.(2022), Décarbonations de la filière sidérurgique : les enjeux du défi de l’« acier vert »,Annale des mines-réalités industrielles, P25
2. P Birât et A. Zaoui (2003), le recyclage de fer, revue de métallurgie internationale, journal of metallurgy, PP33-100.
3. degruyter.com (consulté le 28 novembre2022)
4. Dotchamou, Elodie (2022), comparaison des impacts environnementaux d’une structure biomimétique et d’une structure en poteaux-poutre béton d’un bâtiment tertiaire, mémoire, faculté des sciences appliquées, Université de liège Belge, P50
5. Anthony N. K. (2018). Investir dans le secteur industriel en République Démocratique du Congo, Cahier Sectoriel à Kinshasa, revue, pp 5-28.
6. https:/www. investindrc.cd/fr/mines (Consulté, le 10 juillet 2022)
7. Laskminarayanan A.K. et Vasudevan M. (2018). Advances in Materials and Metallurgy, lecture notes in Mechanical Engineering, p 3.
8. Akinsola S. I., Issa I. O., Adegoke M. A., Ojo V. O. and Alabi A. B. (2016). Characterization of Low Carbon Steel Bar Used For Reinforcing, p19, Journal of the Environment, Vol. 10.
9. Alaneme K.K. (2011). Desing of a Cantilever-Type Rotating Bending Fatigue Testing Maching, Department of Metallurgical and Materials Engeneering, Federal University of Technology, Akure, Nigeria, PMB704, vol 10, No 11, pp1027-1039.
10. Ying J., Xiaofei C., Hangji L., Xianghua R. et Yue Y. L. (2021). Structural Design of Steel Bar Bending Machine, p 6.
11. Sudarsham D. B. (2021). An experiment & FEA of cross sectional area of automotive center consol mounting bracket, Pradnya Surya Engineering Works, Pvt. Ltd., Solapur, Maharashtra, India, p10.
12. Saty D. et Rajeev S. (2021). Optimization of fused deposition modeling (FDM) process parameters for flexural Strength, Department of Mechanical Engineering, Matilal Nehru National Institute of Technology. Allahabad, Prayagraj 21004. volume 44, part 2, pp 3012-3016.
13. BEN-FREDJ (2019). Evolution de la microsctructure des aciers à haute resistance mécanique durant le traitement thermique de trempe, thèse, Université de Québec, Ecole Supérieure de Technologie, pp10-32.
14. Hantcherli M. (2010). Influence d’éléments d’addition sur les transformations de la martensite revenue dans les aciers faiblement alliés. Thèse, Ecole Nationale Supérieure des Mines de Saint Etienne, France, p 125.
15. Naoun M. (2014). Influence du peroxyde d’hydrogène sur la susceptibilité à la corrosion des aciers inoxydables en milieu salin. Thèse, Université Hadj Lakhdar de Batna, p 9.
16. Sekfali S. (2004). Influence de la microstructure sur le comportement local dans les aciers 16MND5. Thèse, Ecole centrale des Arts et Manufactures, Paris, pp 185.
17. Bensaada S. (2019). Elaboration des métaux ferreux, mémoire, Université de Biskra, Algérie, pp 19-52.
18. Bensaada S. (2014). Traitement thermique, classification et désignation des aciers et fontes, livre, Algérie, pp 113.
19. fr (Consulté, le 08 décembre 2022)
20. Akram A. (2017). Caractérisation de l’effet du cuivre pré-allié et pré-mélangé sur la trempabilité des aciers en métallurgie des poudres, mémoire, Université de Laval au Québec, Canada, pp 19.
21. Charlotte Baraudon, Jean-Baptiste Lanfranchi, JM Christian Bastien et Stéphanie Fleck. (2021). Conception d’une echelle francanse d’evaluation de l’utilisabilité des nouvelles technologies éducatives par l’enfant.
22. Mohammed A. (2020). Relation entre la microstructure et les propriétés mécaniques d’acier Duperduplex, influence de la topologie et la fraction de phase inoxydable, livre, Paris, pp 57.
23. Hantcherli M. (2010). Influence d’éléments d’addition sur les transformations de la martensite revenue dans les aciers faiblement alliés. Thèse, Ecole Nationale Supérieure des Mines de Saint Etienne, France, p 125.